The mechanical and electrochemical behavior of ultrasonic spot welded hybrid joints, made of AA5754 aluminum and carbon fiber reinforced epoxy with a co-cured thermoplastic surface layer, was studied. The effect of the welding parameters (energy and force) and the thickness of a thermoplastic film, applied as an upper ply in the composite lay-up, on the development of adhesion strength, was investigated. The best mechanical results were obtained when the welding parameters were able to achieve a large bonding area of mechanical interlocking between naked carbon fibers and aluminum and a better load distribution. The electrochemical results excluded the possibility of galvanic corrosion between aluminum and composite adherends thanks to the insulating action provided by the thermoplastic film

Ultrasonic spot welding of carbon fiber reinforced epoxy composites to aluminum: mechanical and electrochemical characterization

Francesca Lionetto
;
Claudio Mele;Paola Leo;Sonia D'Ostuni;Alfonso Maffezzoli
2018-01-01

Abstract

The mechanical and electrochemical behavior of ultrasonic spot welded hybrid joints, made of AA5754 aluminum and carbon fiber reinforced epoxy with a co-cured thermoplastic surface layer, was studied. The effect of the welding parameters (energy and force) and the thickness of a thermoplastic film, applied as an upper ply in the composite lay-up, on the development of adhesion strength, was investigated. The best mechanical results were obtained when the welding parameters were able to achieve a large bonding area of mechanical interlocking between naked carbon fibers and aluminum and a better load distribution. The electrochemical results excluded the possibility of galvanic corrosion between aluminum and composite adherends thanks to the insulating action provided by the thermoplastic film
File in questo prodotto:
File Dimensione Formato  
2.pdf

accesso aperto

Descrizione: post-print
Tipologia: Post-print referato (Refereed author’s manuscript)
Licenza: Creative commons
Dimensione 45.3 MB
Formato Adobe PDF
45.3 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/419767
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 111
  • ???jsp.display-item.citation.isi??? 101
social impact