Different hybrid epoxy formulations were produced and cold-cured, monitoring the properties development during low temperature curing and aging. All systems were based on silane functionalized bis-phenol A (DGEBA) resins (Part A), cured at ambient temperature with two amine hardeners (Part B). The different components of the formulations were selected on their potential capability to bring about enhancements in the glass transition temperature. The durability of the produced hybrids was probed in comparison to the corresponding neat epoxies by monitoring changes in glass transition temperature (Tg) and flexural mechanical properties after exposure to different levels of humidity and immersion in water and at temperatures slightly higher than the local ambient temperature, in order to simulate the conditions encountered during summer seasons in very humid environments. The thermal degradation resistance of the hybrid systems was also evaluated by thermogravimetric analysis.
Experimental Cold-Cured Nanostructured Epoxy-Based Hybrid Formulations: Properties and Durability Performance
Frigione, Mariaenrica
;Lettieri, Mariateresa;Lionetto, Francesca;
2020-01-01
Abstract
Different hybrid epoxy formulations were produced and cold-cured, monitoring the properties development during low temperature curing and aging. All systems were based on silane functionalized bis-phenol A (DGEBA) resins (Part A), cured at ambient temperature with two amine hardeners (Part B). The different components of the formulations were selected on their potential capability to bring about enhancements in the glass transition temperature. The durability of the produced hybrids was probed in comparison to the corresponding neat epoxies by monitoring changes in glass transition temperature (Tg) and flexural mechanical properties after exposure to different levels of humidity and immersion in water and at temperatures slightly higher than the local ambient temperature, in order to simulate the conditions encountered during summer seasons in very humid environments. The thermal degradation resistance of the hybrid systems was also evaluated by thermogravimetric analysis.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.